Nickel-Based Superalloy and Heat Treatment for Salt Environments

ABSTRACT

An alloy has, by weight: nickel (Ni) as a largest constituent; 6.7% to 7.5% chromium; 1.8% to 2.3% molybdenum; 4.75% to 10.3% cobalt; 5.3% to 5.9% aluminum; 2.8% to 3.2% rhenium; 3.7% to 7.3% tungsten; and 6.0% to 9.0% tantalum.

CROSS-REFERENCE TO RELATED APPLICATION

Benefit is claimed of U.S. Patent Application No. 62/829,821, filed Apr. 5, 2019, and entitled “Nickel-Based Superalloy and Heat Treatment for Salt Environments”, the disclosure of which is incorporated by reference herein in its entirety as if set forth at length.

BACKGROUND

The disclosure relates to gas turbine engines. More particularly, the disclosure relates to alloy selection and crystalline orientation for gas turbine engine components.

Gas turbine engine hot section components are commonly formed of alloys, typically nickel- or cobalt-based superalloys. Many components, such as blades are formed of single-crystal (SX) alloys. In such single-crystal components, essentially the entire component is formed of a single continuous crystal lattice. Typically, the orientation of that lattice is predetermined to achieve desired properties of the component. The orientation may be assured by use of a grain starter or other casting techniques.

By way of example, U.S. Pat. No. 4,605,452 of Gemma and Dierberger identifies face centered cubic (FCC) single-crystal gas turbine blades wherein the [110] crystal axis is tangent to the blade airfoil surface in a critical crack-prone region just behind the leading edge of the airfoil at about 40-80% of the airfoil span. U.S. Pat. No. 6,074,602 (the '602 patent) of Wukusick and Buchakjian, Jr., identifies a further single-crystal alloy. Table I (discussed below) includes comparative data from an alloy of the '602 patent among others.

SUMMARY

One aspect of the disclosure involves an alloy comprising, by weight: nickel (Ni) as a largest constituent; 6.7% to 7.5% chromium; 1.8% to 2.3% molybdenum; 4.75% to 10.3% cobalt; 5.3% to 5.9% aluminum; 2.8% to 3.2% rhenium; 3.7% to 7.3% tungsten; and 6.0% to 9.0% tantalum.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the alloy comprising, by weight: nickel (Ni) as said largest constituent; 6.8% to 7.2% chromium; 1.8% to 2.2% molybdenum; 4.9% to 10.2% cobalt; 5.35% to 5.7% aluminum; 2.9% to 3.1% rhenium; 3.8% to 7.2% tungsten; and 6.1% to 8.9% tantalum.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight, one or more of: a titanium content, if any, being no more than 0.50%; a boron content, if any, being no more than 0.01%; a yttrium content, if any, being no more than 0.02%; a sulfur content, if any, being no more than 5 ppm; a hafnium content, if any being no more than 0.50%; a silicon content, if any, being no more than 0.50%; and a carbon content, if any, being no more than 0.10%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight, one or more of: a sulfur content, if any, being no more than 1 ppm; a hafnium content being 0.050% to 0.15%; a silicon content, if any, being no more than 0.30%; and a carbon content, if any, being no more than 0.10%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: a combined content, if any, of elements other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, being no more than 1.0%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: a combined content, if any, of elements other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, being no more than 0.75%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: an individual content, if any, of every element other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, being no more than 0.50%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: an individual content, if any, of every element other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, being no more than 0.40%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of chromium, cobalt, and aluminum being 17.0% to 23.0%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of chromium, cobalt, and aluminum being 17.5% to 22.5%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of tungsten and tantalum being 8.0% to 14.0%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of tungsten and tantalum being 12.0% to 13.0%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of rhenium, tungsten, and tantalum being 9.0% to 16.5%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: the combined content of rhenium, tungsten, and tantalum being 10.0% to 15.5%.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include, by weight: yttrium, lanthanum, and/or cerium up to 0.05% combined.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the alloy having one to-all of: an average 1500 F/90 ksi salt rupture life of at least 450 hours; and an average 1500 F/100 ksi salt rupture life of at least 150 hours; an average 1800 F/36 ksi air rupture life of at least 150 hours; and an average 1850 F/38 ksi air rupture life of at least 40 hours.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the alloy having one-to-all of: an average 1500 F/90 ksi salt rupture life of at least 300 hours; and an average 1500 F/100 ksi salt rupture life of at least 100 hours; an average 1800 F/36 ksi air rupture life of at least 140 hours; and an average 1850 F/38 ksi air rupture life of at least 38 hours.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the alloy of in single-crystal (SX) form.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include a turbine blade comprising a substrate formed of the alloy.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the turbine blade comprising: an attachment root; an airfoil extending from a proximal end to a tip; and a platform between the airfoil and the attachment root.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the turbine blade further comprising: a thermal barrier coating atop the substrate at least along the airfoil.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the thermal barrier coating not being along the root and platform underside.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the alloy, heat treated by a method comprising: a solution heat treat for a period of at least 4.0 hours; and after the solution heat treat, an intermediate heat treatment at 1950 F to 2075 F for 3.5 hours to 4.5 hours followed by a final aging precipitation heat at a temperature of 1575 F to 1675 F for a period of 4.0 hours to 32.0 hours.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the precipitation heat being at a temperature of 1575 F to 1675 F for a period of 8.0 hours to 32.0 hours.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the solution heat treat being at least 20 F over solvus.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include a method for using the alloy, the method comprising: a solution heat treat for a period of at least 4.0 hours; and after the solution heat treat, a final aging precipitation heat at a temperature of 1575 F to 1675 F for a period of 4.0 hours to 32.0 hours.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the method being effective to improve rupture performance in salt environments relative to a pure precipitation heat treat.

A further embodiment of any of the foregoing embodiments may additionally and/or alternatively include the method being effective to improve rupture performance in salt environments relative to a solution heat treat of 2.0 hours or less followed by precipitation heat treat otherwise under like conditions.

The details of one or more embodiments are set forth in the accompanying drawings and the description below. Other features, objects, and advantages will be apparent from the description and drawings, and from the claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a view of a turbine blade.

Like reference numbers and designations in the various drawings indicate like elements.

DETAILED DESCRIPTION

In FIG. 1, an engine turbine element 20 is illustrated as a blade having an airfoil 22 which extends between an inboard end 24, and an opposing outboard end 26 (e.g., at a free tip), a distance therebetween extending substantially in the engine radial direction. The airfoil also includes a leading edge 28 and an opposing trailing edge 30. A pressure side 32 and an opposing suction side 34 extend between the leading edge 28 and trailing edge 30.

The airfoil inboard end 24 is disposed at the outboard surface 40 of a platform 42. An attachment root 44 extends radially inward from the underside 46 of the platform.

The root 44 has an inner diameter (ID) end or face 48, an upstream axial end 50, a downstream axial end 52, and first and second lateral sides 54 and 56, respectively. The root 44 is complementary to a disk slot (not shown). When fully seated in the disk slot, the faces 50 and 52 may face exactly forward/upstream and rearward/downstream in the engine frame of reference. Depending on disk configuration (slot orientation), the sides may extend parallel to the engine centerline between the axial ends (root having a rectangular footprint/section) or may extend skew (root having a non-right parallelogram footprint) such as in the illustrated example.

The turbine blade is cast of a high temperature alloy, namely a single-crystal Ni-based superalloy discussed below.

The blade may also have a thermal barrier coating (TBC, e.g., one or more layer ceramic atop of one or more layer bondcoat) system along at least a portion of the airfoil.

The blade may have an internal cooling passageway system (not shown) extending from one or more inlets along a root to a plurality of outlets (along or mostly along the airfoil and platform surfaces).

Stress corrosion cracking (SCC) has been a concern in commercial engine turbine blades. Atmospheric salt and pollution appear to be contributing factors. A particular area of SCC is along platform undersides of high pressure turbine (HPT) blades.

A number of alloys were conceived as potentially offering improved resistance to stress corrosion cracking, particularly in salt environments. Table I shows test data for ten candidate alloys (Ex. 1-10) and four prior art alloys (Prior Art 1-4). Of the examples, Ex. 7, 9, and 10 show particular benefits discussed below.

Table I lists the post-solutioning heat treatments used. For example, “2050 F/4+1975 F/4+1650 F/4” indicates 2050° Fahrenheit for four hours followed by 1975° Fahrenheit for four hours followed by 1650° Fahrenheit for four hours. The solutioning involved heat treatment at or above the alloy gamma prime solvus temperatures for 4.0 hours in the 2350° to 2375° Fahrenheit range.

Rupture tests were performed on creep-rupture specimens with nominal 0.125 inch gauge diameters tested isothermally at 1500 F with constant load and low melting eutectic salt mixture brushed on the gauge section every 100 hours. The salt was a quaternary system of sodium, magnesium, potassium, and calcium sulfates with a melting point of about 1200 F (e.g., 1175 F-1225 F or 1195 F to 1205 F). The salt represents an approximately equal blend of two ternary examples from the cited Du article below (rows 5 and 6 of Table 4 of the Du article). The air rupture test was performed in a furnace drawing in ambient laboratory air; whereas the salt rupture test was performed in a similar arrangement although salt was brushed on the gauge section periodically. Such salt and test procedure may be used as a reference in the tests of the claims below. Alternative reference salts are disclosed in BORNSTEIN, NORMAN S. “Reviewing sulfidation corrosion—Yesterday and today”, Journal of Materials (Jom), November, 1996, pages 37-39, Volume 48, Issue No. 11, Springer, Heidelberg, Germany and DU, H., “Thermodynamic assessment of the K₂SO₄—Na2SO₄—MgSO₄—CaSO₄ system”, Journal of Phase Equilibria, Jan. 1, 2000, pages 6-18, Volume 21, Issue No. 1, Springer, Heidelberg, Germany. The disclosures of said Bornstein and Du articles are incorporated by reference in their entireties herein as if set forth at length. Similar relative behavior of alloys and heat treatments would be expected when tested with the Bornstein and Du salts to the results obtained herein.

Two factors to be considered from the tests are absolute rupture life and consistency in rupture life. Because of the relatively close compositions of the examples and prior art, what would otherwise be a statistically insignificantly small sample size of one alloy (e.g., one or two tests) allows a statistically significant conclusion to be made when such small test numbers of many slightly different alloys are considered. Thus, running only two tests each of two alloys would not be statistically significant if one alloy had a 300-hour test life and a 250-hour test life while the other had a 300-hour test life and a 50-hour test life. But, such two-test per alloy data becomes significant when one looks a greater number of alloys. From such data one may statistically significantly determine a compositional range associated with the long life and/or consistent performance. In this case, a compositional range around Ex. 7, 9, and 10 is indicated as having an advantageous combination of life and consistency.

In contrast, consider Ex. 1, 2 and 3 where Cr levels below 6.75% produced instances of lower rupture lives in salted creep testing.

In Table I, the three targeted alloys (Ex. 7, 9, and 10) have significant amounts of the elements Ni, Cr, Mo, W, Ta, Al, Co, and Re. As far as other elements, Ti, C, B, Y, and/or Hf can be added in small amounts to benefit alloy properties. S should be kept as low as possible to benefit oxidation resistance. Small Si additions will also benefit oxidation resistance. Combined Y+Hf+B+Si additions should be maintained below 0.40% to achieve high levels of alloy incipient melting temperature. In terms of individual contents, in exemplary ranges one-to-all of a titanium content, if any, is no more than 0.50%; a boron content, if any, is no more than 0.01%; a yttrium content, if any, is no more than 0.02%; a sulfur content, if any, is no more than 5 ppm or no more than 1 ppm; a hafnium content, if any is no more than 0.50% or is in the range of 0.050% to 0.15%; a silicon content, if any, is no more than 0.50% or 0.30%; and a carbon content, if any, is no more than 0.10%, by weight.

In various examples, a combined weight content, if any, of elements other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, is no more than 1.0% or 0.75% or 0.50% or 0.40%.

In various examples, the combined weight content of chromium, cobalt, and aluminum is 17.0% to 23.0% or 17.5% to 22.5% or 20.0% to 22.0%.

In terms of heat treatment, from Table I it can be further determined that an advantageous heat treatment involves full or close to full gamma prime solutioning at temperatures at or above 2375 F, followed by intermediate heat treatments at 2050 F and or 1975 F for 4 hours with a final PHT aging heat treatment at 1650 F for 4 hours.

As a further refinement, Table III involves exploration of heat treatment parameters with the Prior Art 3 alloy. Solution heat treat is at a temperature between solvus and incipient melting point. At commercial scale to have an effective heat treat, solutioning may be at a temperature of at least 20 F over solvus or at least 25 F or at least 30 F. At the other end, to avoid errors (risk of incipient melting due to process variation), a target solution heat treat may be in the range of not more than 40 F below incipient melting or not more than 35 F or not more than 30 F or not more than 25 F.

The Prior Art 3 alloy has a 2440 F incipient melting temperature and a 2370 F solvus temperature. Exemplary solution heat treat is 2400 F up to the incipient melting temperature. At commercial scale to avoid errors, a target solution heat treat may be in the range of 2380 F to 2415 F. Times of 30 minutes, 4 hours, and 20 hours are given. High consistency is seen at 20 hours. Alternative exemplary lower ends on ranges other than 4 hours are 6 hours and 8 hours. Much above 20 would seem to offer little benefit for cost.

Several pure precipitation heat treatments (PHT) are compared with several solution heat treatments. The latter are followed by a two-stage final heat treatment. In the same salt tests as those of Table I, it is seen that the increasing alloy homogenization by increasing the time at the solution heat treatment temperature reduces variability and increases average life. The post-solutioning final aging heat treatment (a precipitation heat treat (PHT)) also plays a significant role in increasing both the minimum and average rupture life in salt tests. Increasing both the PHT temperature to 1600 F and the time to 32 hours produces the highest creep-rupture life in a salt environment.

When transferring this Prior Art 3 experience to the other alloys, adjustments may be made for differences in solutioning temperature and incipient melting point. For example, Examples 7, 9, and 10 have lower solvus and incipient meting temperatures which would have corresponding lower target heat treatment temperatures while preserving times.

Alloys to be used in turbine blade applications require good high temperature creep-rupture strength in an air environment. Key Table I examples also show good high temperature creep-rupture life as shown in testing conducted at 1800 F/36 ksi and 1850 F/38 ksi. Although lives are not as good as those in the alloy of Prior Art 3, they are adequate to meet service turbine blade requirements. We infer that these good lives can be maintained by insuring that total W+Ta+Re content stays in the range of 9.0 to 16.5% by weight. Total W+Ta content may more narrowly stay in the range of 12.0% to 13.0% by weight or more broadly 8.0% to 14.0% (with life compromise at the low end).

TABLE I Alloy Rupture Tests (Salt and Air) Up to Two Tests at each of Two Conditions per Heat Treat Tested Elemental Weight Percentage Alloy Ni Cr Ti Mo W Ta Al Co Re Hf C B Y Ex. 1 Bal 6.03 0 1.94 6 6.33 5.68 10.02 2.93 0.09 0.03 <0.01 <0.001 Ex. 2 Bal 6.45 0 1.93 5.89 6.27 5.65 10.04 2.99 0.09 0.03 <0.01 <0.001 Ex. 3 Bal 6.73 0 1.94 5.97 6.3 5.62 9.97 3.03 0.09 0.03 <0.01 <0.001 Ex. 4 Bal 7.55 0 1.92 5.94 6.33 5.63 10 2.99 0.09 0.03 <0.01 <0.001 Ex. 5 Bal 7.94 0 1.95 6.02 6.28 5.61 10 2.98 0.1 0.03 <0.01 <0.001 Ex. 6 Bal 6.97 0 1.93 5.95 6.28 5.61 7.55 3.02 0.09 0.03 <0.01 <0.001 Ex. 7 Bal 6.88 0 1.95 5.94 6.25 5.57 5.06 3.06 0.09 0.03 <0.01 <0.001 Ex. 8 Bal 5.99 0 2.07 5.97 6.31 5.6 7.56 3.05 0.09 0.03 <0.01 <0.001 Ex. 9 Bal 7.0 0 2.0 4.0 8.8 5.6 10.1 3.0 0.11 0.03 <0.01 <0.001 Ex. 10 Bal 7.1 0 2.1 7.0 6.2 5.4 10.0 3.0 0.11 0.03 <0.01 <0.001 Prior Bal 8 1.5 2 8 6 5 5 0 Art 1 Prior Bal 6.5 1 0.6 6 6.5 5.6 9 3 Art 2 Prior Bal 5 0 1.9 5.9 8.9 5.65 10 2 0.03 0.03 <0.01 <0.001 Art 3 Prior Bal 7 0 1.5 5 6.5 6.2 7.5 3 0.15 0.05 0.004 0.02 Art 4 Test (hours) Salt Rupture Air Rupture Tested Post-Solution Heat Treat 1500 F.- 1500 F.- 1800 F.- 1850 F.- Alloy (Temp/Hours) 90 ksi 100 ksi 36 ksi 38 ksi Ex. 1 1975 F./4 + 1500 F./8 214.8 0.6 188.3 42.3 15.3 3 188.9 40.8 2050 F./4 + 1975 F./ 240.5 3.3 202.4 43.3 4 + 1650 F./4 226.9 0.8 214.7 47.7 1975 F./4 + 1650 F./4 235.6 105.5 296 101.4 Ex. 2 1975 F./4 + 1500 F./8 1.2 0.6 193.7 49.8 239.2 3.4 198.3 40.6 2050 F./4 + 1975 F./ 230.5 115.3 159.1 51.7 4 + 1650 F./4 117.5 1.2 191.7 46.7 1975 F./4 + 1650 F./4 341.6 116.9 299.2 93.5 Ex. 3 1975 F./4 + 1500 F./8 255.9 0.7 232.8 54.4 2.3 2.9 281.4 52.2 2050 F./4 + 1975 F./ 441.3 95.6 275.8 52.8 4 + 1650 F./4 205.9 108.7 246.2 56.2 1975 F./4 + 1650 F./4 416.2 40.8 351 214.3 Ex. 4 1975 F./4 + 1500 F./8 298.8 124.9 182.1 39.9 405.8 114.8 186.5 41.5 2050 F./4 + 1975 F./ 205.1 134.8 195.5 37.8 4 + 1650 F./4 90.5 115.1 186.3 41.1 1975 F./4 + 1650 F./4 114.5 195.5 579.4 145.9 Ex. 5 1975 F./4 + 1500 F./8 363.9 113.2 136.4 32.2 468.1 127.0 140.7 2050 F./4 + 1975 F./ 233.8 132.6 140.1 36.6 4 + 1650 F./4 376.9 150.9 142.7 34.8 1975 F./4 + 1650 F./4 207.3 115.3 483.5 160.8 Ex. 6 1975 F./4 + 1500 F./8 297.4 95.5 202.0 43.1 385.3 0.7 188.4 42.5 2050 F./4 + 1975 F./ 231.5 133.3 167.5 41.6 4 + 1650 F./4 206.1 90.6 180.8 1975 F./4 + 1650 F./4 114.8 128.0 188.9 186.6 Ex. 7 1975 F./4 + 1500 F./8 322.1 140.1 163.6 42.1 356.2 115.2 196.4 2050 F./4 + 1975 F./ 455.7 144.1 149.6 40.4 4 + 1650 F./4 348.8 97.0 165.3 41.9 1975 F./4 + 1650 F./4 533.7 138.9 496.6 208.1 Ex. 8 1975 F./4 + 1500 F./8 256.8 106.2 194.4 43.3 232.0 10.1 186.7 48.4 2050 F./4 + 1975 F./ 255.3 107.1 209.8 51.1 4 + 1650 F./4 230.5 51.8 169.5 44.0 1975 F./4 + 1650 F./4 245.6 1.5 210.8 132.6 Ex. 9 1975 F./4 + 1500 F./8 682.2 251.9 2050 F./4 + 1975 F./ 803.3 4 + 1650 F./4 Ex. 10 1975 F./4 + 1500 F./8 430.2 299.2 2050 F./4 + 1975 F./ 490.0 4 + 1650 F./4 237.1 Prior 1975 F./4 + 1550 F./24 234.3 Art 1 227.8 Prior 2085 F./2 + 1600 F./20 0.1 Art 2 71.9 206.5 Prior 1975 F./4 + 1500 F./8  0.7 min* 306 85.0 Art 3 401 max 1975 F./4 + 1600 F./32 92.6 min 517 max Prior 1975 F./4 + 1500 F./8 263.9 Art 4 2050 F./4 + 1975 F./ 247.3 150.0 45.0 4 + 1650 F./4 2050 F./4 + 1975 F./ 410.1 4 + 1650 F./4 Prior Art 3 involved many samples and only the min. and max values are listed.

TABLE II Alloy Compositional Ranges Elemental Weight Percentage Range Ni Cr Mo W Ta Al Co Re Hf C B Y Range 1A Bal 6.7-7.5 1.8-2.3 3.7-7.3 6.0-9.0 5.3-5.9 4.75-10.3  2.8-3.2 0.08-0.15 0.03 <0.01 <0.001 Range 1B Bal 6.8-7.2 1.8-2.2 3.8-7.2 6.1-8.9 5.35-5.7  4.9-10.2 2.9-3.1 0.09-0.12 Range 2A Bal 6.7-7.2 1.8-2.1 5.75-6.25 6.0-6.5 5.4-5.7 4.75-5.25  2.9-3.2 0.08-0.12 Range 2B Bal 6.8-7.1 1.85-2.0  5.8-6.1 6.1-6.4 5.5-5.7 4.9-5.2  3.0-3.2 0.08-0.11 Range 3A Bal 6.8-7.2 1.8-2.2 3.7-4.3 8.7-9.0 5.4-5.8 9.8-10.3 2.9-3.2 0.09-0.13 Range 3B Bal 6.9-7.1 1.9-2.1 3.8-4.2 8.7-8.9 5.5-5.7 9.9-10.1 2.9-3.1 0.10-0.12 Range 4A Bal 6.8-7.3 1.9-2.3 6.8-7.3 6.0-6.5 5.3-5.6 9.8-10.2 2.9-3.2 0.09-0.13 Range 4B Bal 6.9-7.2 2.0-2.2 6.9-7.1 6.1-6.3 5.3-5.S 9.9-10.1 2.9-3.1 0.10-0.12

TABLE III Effect of heat Treatment on Prior Art 3 Min. and Max. Rupture Life (Hours) in Salt at 1500 F.-90 ksi Rupture Final Number Life Heat Treat Heat Treat Heat Treat of (Hours) Type Parameters (FHT)* Samples Min. Max. N/A (As-Cast)   N/A Y 3 1.1 236.0 Precipitation 1300 F./24 hrs N/A 8 0.3 94.3 1500 F./8 hrs  N/A 29 1.1 401.2 1600 F./8 hrs  N/A 30 0.8 522.7 1600 F./32 hrs N/A 27 92.6 517.0 Solution  2400 F./30 min Y 2 130.1 340.2   2400/4 hrs Y 2 327.7 398.7 2400 F./20 hrs Y 2 399 406.5 *1975 F./4 hrs + 1600 F./32 hrs

The use of “first”, “second”, and the like in the following claims is for differentiation within the claim only and does not necessarily indicate relative or absolute importance or temporal order. Similarly, the identification in a claim of one element as “first” (or the like) does not preclude such “first” element from identifying an element that is referred to as “second” (or the like) in another claim or in the description.

One or more embodiments have been described. Nevertheless, it will be understood that various modifications may be made. For example, when applied to an existing baseline configuration, details of such baseline may influence details of particular implementations. Accordingly, other embodiments are within the scope of the following claims. 

What is claimed is:
 1. An alloy comprising, by weight: nickel (Ni) as a largest constituent; 6.7% to 7.5% chromium; 1.8% to 2.3% molybdenum; 4.75% to 10.3% cobalt; 5.3% to 5.9% aluminum; 2.8% to 3.2% rhenium; 3.7% to 7.3% tungsten; and 6.0% to 9.0% tantalum.
 2. The alloy of claim 1 comprising, by weight: nickel (Ni) as said largest constituent; 6.8% to 7.2% chromium; 1.8% to 2.2% molybdenum; 4.9% to 10.2% cobalt; 5.35% to 5.7% aluminum; 2.9% to 3.1% rhenium; 3.8% to 7.2% tungsten; and 6.1% to 8.9% tantalum.
 3. The alloy of claim 1 wherein, by weight, one or more of: a titanium content, if any, is no more than 0.50%; a boron content, if any, is no more than 0.01%; a yttrium content, if any, is no more than 0.02%; a sulfur content, if any, is no more than 5 ppm; a hafnium content, if any is no more than 0.50%; a silicon content, if any, is no more than 0.50%; and a carbon content, if any, is no more than 0.10%.
 4. The alloy of claim 1 wherein, by weight, one or more of: a sulfur content, if any, is no more than 1 ppm; a hafnium content is 0.050% to 0.15%; a silicon content, if any, is no more than 0.30%; and a carbon content, if any, is no more than 0.10%.
 5. The alloy of claim 1 wherein, by weight: a combined content, if any, of elements other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, is no more than 1.0%.
 6. The alloy of claim 1 wherein, by weight: a combined content, if any, of elements other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, is no more than 0.75%.
 7. The alloy of claim 1 wherein, by weight: an individual content, if any, of every element other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, is no more than 0.50%.
 8. The alloy of claim 1 wherein, by weight: an individual content, if any, of every element other than nickel, chromium, cobalt, aluminum, rhenium, tungsten, tantalum, molybdenum, if any, sulfur, if any, hafnium, if any, silicon, if any, and carbon, if any, is no more than 0.40%.
 9. The alloy of claim 1 wherein, by weight: the combined content of chromium, cobalt, and aluminum is 17.0% to 23.0%.
 10. The alloy of claim 1 wherein, by weight: the combined content of chromium, cobalt, and aluminum is 17.5% to 22.5%.
 11. The alloy of claim 10 wherein, by weight: the combined content of tungsten and tantalum is 8.0% to 14.0%.
 12. The alloy of claim 10 wherein, by weight: the combined content of tungsten and tantalum is 12.0% to 13.0%.
 13. The alloy of claim 1 wherein, by weight: the combined content of rhenium, tungsten, and tantalum is 9.0% to 16.5%.
 14. The alloy of claim 13 wherein, by weight: the combined content of rhenium, tungsten, and tantalum is 10.0% to 15.5%.
 15. The alloy of claim 1 further comprising, by weight: yttrium, lanthanum, and/or cerium up to 0.05% combined.
 16. The alloy of claim 1 having one to-all of: an average 1500 F/90 ksi salt rupture life of at least 450 hours; and an average 1500 F/100 ksi salt rupture life of at least 150 hours; an average 1800 F/36 ksi air rupture life of at least 150 hours; and an average 1850 F/38 ksi air rupture life of at least 40 hours.
 17. The alloy of claim 1 having one-to-all of: an average 1500 F/90 ksi salt rupture life of at least 300 hours; and an average 1500 F/100 ksi salt rupture life of at least 100 hours; an average 1800 F/36 ksi air rupture life of at least 140 hours; and an average 1850 F/38 ksi air rupture life of at least 38 hours.
 18. The alloy of claim 1 in single-crystal (SX) form.
 19. A turbine blade comprising a substrate formed of the alloy of claim 1 and further comprising: an attachment root; an airfoil extending from a proximal end to a tip; a platform between the airfoil and the attachment root; and a thermal barrier coating atop the substrate at least along the airfoil, wherein: the thermal barrier coating is not along the root and platform underside.
 20. The alloy of claim 1, heat treated by a method comprising: a solution heat treat for a period of at least 4.0 hours; and after the solution heat treat, an intermediate heat treatment at 1950 F to 2075 F for 3.5 hours to 4.5 hours followed by a final aging precipitation heat at a temperature of 1575 F to 1675 F for a period of 4.0 hours to 32.0 hours. 